E-glass Assembled Roving For Chopping
E-glass Assembled Roving For Chopping
Assembled Roving for Chopping is coated with special silane-based sizing, compatible with UP and VE, delivering relatively high resin absorbability and excellent choppability, while its final composite products deliver superior water resistance and excellent chemical corrosion resistance.
Features
●High resin absorbability
●Excellent choppability
●Superior water resistance
● excellent chemical corrosion resistance of final products
Application
It is typically used to manufacture FRP pipes.
Product List
|
Item |
Linear Density |
Resin Compatibility |
Features |
End Use |
|
BHC-01A |
2400, 4800 |
UP, VE |
good dispersion, moderate wet out in resin, good static control |
FRP pipes |
|
BHC-02A |
2400, 4800 |
UP, VE |
few fuzz, good choppability, excellent chemical resistance |
as chop roving for pipe manufacture |
| Identification | |
| Type of Glass |
E |
| Assembled Roving |
R |
| Filament Diameter, μm |
13 |
| Linear Density, tex |
2400, 4800 |
| Technical Parameters | |||
|
Linear Density (%) |
Moisture Content (%) |
Size Content (%) |
Stiffness (mm) |
|
ISO 1889 |
ISO 3344 |
ISO 1887 |
ISO 3375 |
|
±6 |
≤0.15 |
1.20±0.15 |
125±20 |
Filament Winding Process
Traditional Filament Winding
In the filament winding process , continuous strands of resin-impregnated glassfiber are wound under tension onto a mandrel in precise geometric patterns tobuild up the part which is then cured to form the finished parts.
Continuous Filament Winding
Multiple laminate layers , composed of resin , reinforcement glass and other materials are applied to a rotating mandrel , which is formed from a continuous steel band continuously traveling in a cork-screw motion . The composite part is heated and cured in place as the mandrel travels through the line and then cut into a specific length with a traveling cut-off saw .